Product Details:
|
| Name: | Ceramic Shaft Seal | Feature: | Heat Resistance |
|---|---|---|---|
| Color: | White Or Black | Temperature: | 1400 ℃ |
| Vickers Hardness: | Alumina 1800-2000 HV; Zirconia ≈1300 HV; Silicon Carbon ≈2500HV | Fracture Toughness: | Alumina ≈5 (Mpa M1/2) ; Zirconia 7 (Mpa M1/2) |
| Compressive Strength: | Alumina ＞3200 (Mpa Psi*103); Zirconia ≈3900 (Mpa Psi*103)；Silicon Carbon 2200 (Mpa Psi*103) | Thermal Expending Coefficient: | Alumina 7.8-8.2 （1*10^-6/℃）；Silicon Carbon ≈4.5 （1*10^-6/℃） |
| High Light: | 3100Mpa Ceramic Shaft Seal,1400 ℃ Ceramic Shaft Seal,3100Mpa aluminium oxide ceramic |
||
Alumina Ceramic Pump Seal Part Pump Component Anti-corrosion
Introduction
1) Pump type:Water pumps and household pumps
2) Our high quality Burgmann Mechanical Seal can replace the orignal seals
3) The standard is according to Din24960ISO3069,EN12576,API682
4) OEM small order is avaiable
5) Factory supplying with low price and fast shipping time
Properties:
Powerful interatomic bonds endows zirconia ceramics not only with high hardness and wear resistance, but also a resistance to corrosion. Usually it has less hardness and brittleness than that of alumina ceramic, but has more elasticity, which means it is not as brittle as alumina ceramic. If hardness is not so exacting, zirconia parts are a good choice to be applied.
| Ceramic 95% | |
| Alumina | |
| Fundamental properties | High hardness, good wear resistance under abrasion,low electrical conductivity,good value for money |
| Main component | 95% Al2O3 |
| Gross density | 3.7g/cm^3 |
| Flexural Strength | 400 Mpa (Psi*103) |
| Compressive Strength | 3100Mpa (Psix103) |
| Fracture Toughness | 5 Mpa m1/2 |
| Young’s Modulus (dynamic)/Elasticity Modules | 300 Gpa |
| Vickers Hardness | 1500-2200 HV |
| Thermal Conductivity | 28 W/mK |
| Coefficient of Linear Expansion (20–400°C) |
7.5 10^–6 K–1 |
| Maximum Operating Temperature | 1400 ℃ |
| Thermal Expanding Coefficient | 7.5 (1x10^-6/℃) |
| Thermal Shock Resistance | 250℃ Tc |
| Disruptive Strength | KV/mm,DC ≥20 |
| Acid Resistance | mg/cm^2 ≤0.7 |
| Alkali Resistance | mg/cm^2 ≤0.2 |
| Wear Resistance | g/cm^2 ≤0.1 |
| Dielectric Strength | 9.0 εr(20℃ ,1MHz) |
| Dielectric Constant | 9.2 1MHz 25° |
| Tensile Strength | 51KN |
| Volume Resistivity | ＞10^15 100° |
| Water Absorption | 0 |
| Specific Heat Capacity | 0.78x10^3 J/(kg.K) |
Application:
Because zirconia has good properties of elasticity module and high hardness, as well as the above good properties, the parts made from zirconia are often used as mechanical or pump seal plate or disc.
About Us
Suzhou Jingci Super Hard Materials Co., Ltd has specialized in precision ceramics for more than twenty years and has rich experiences in designing and developing technical ceramic solutions for a wide variety of applications. Jingci has the capability to provide customers with expertise to make sure the best design and materials are made for their specific application and needs