Product Details:
|
| Name: | Ceramic Seal Ring | Material: | Al2o3 |
|---|---|---|---|
| Color: | White Or Black | Density: | Alumina 3.7-3.9g/cm^3; Zirconia ≈6g/cm^3; Silicon Carbon ≈3.14g/cm^3 |
| Vickers Hardness: | Alumina 1800-2000 HV; Zirconia ≈1300 HV; Silicon Carbon ≈2500HV | Fracture Toughness: | Alumina ≈5 (Mpa M1/2) ; Zirconia 7 (Mpa M1/2) |
| Compressive Strength: | Alumina ＞3200 (Mpa Psi*103); Zirconia ≈3900 (Mpa Psi*103)；Silicon Carbon 2200 (Mpa Psi*103) | Usage: | Circulating |
| High Light: | 96% Ceramic Pump Seal,Al2o3 Ceramic Pump Seal,Al2o3 Ceramic Seal ring |
||
96% Alumina Ceramic Pump Seal Ring Pump Component Circulating Pump Anti-corrosion
Introduction
The ceramic face seal ring is to plug the gap between the housing and the rotating shaft so tightly that no liquid or gas may escape. This leakproof seal is achieved by means of a rotating sealing surface at the point of shaft entry. With their outstanding thermal conductivity, low heat expansion coefficient and high Young's modulus, high-performance ceramics minimize any deformation to the face seal or packing ring under mechanical and thermal loads. Alongside such resistance to corrosive media it is the tribological properties of the sealing system that figure predominantly in the selection of material. The important factor is whether or not the seal gap is lubricated by a fluid medium (be it liquid or gas). For this reason there is standard combination of materials. If there is lubrication in the system, ceramic to ceramic matings are possible. In other instances, one of the two componentsmust possess lubricating properties. One well proven combination consists of ceramics to carbon graphite.
| Ceramic 95% | |
| Alumina | |
| Fundamental properties | High hardness, good wear resistance under abrasion,low electrical conductivity,good value for money |
| Main component | 95% Al2O3 |
| Gross density | 3.7g/cm^3 |
| Flexural Strength | 400 Mpa (Psi*103) |
| Compressive Strength | 3100Mpa (Psix103) |
| Fracture Toughness | 5 Mpa m1/2 |
| Young’s Modulus (dynamic)/Elasticity Modules | 300 Gpa |
| Vickers Hardness | 1500-2200 HV |
| Thermal Conductivity | 28 W/mK |
| Coefficient of Linear Expansion (20–400°C) |
7.5 10^–6 K–1 |
| Maximum Operating Temperature | 1400 ℃ |
| Thermal Expanding Coefficient | 7.5 (1x10^-6/℃) |
| Thermal Shock Resistance | 250℃ Tc |
| Disruptive Strength | KV/mm,DC ≥20 |
| Acid Resistance | mg/cm^2 ≤0.7 |
| Alkali Resistance | mg/cm^2 ≤0.2 |
| Wear Resistance | g/cm^2 ≤0.1 |
| Dielectric Strength | 9.0 εr(20℃ ,1MHz) |
| Dielectric Constant | 9.2 1MHz 25° |
| Tensile Strength | 51KN |
| Volume Resistivity | ＞10^15 100° |
| Water Absorption | 0 |
| Specific Heat Capacity | 0.78x10^3 J/(kg.K) |
Advantages of zirconia parts:
·High wear, heat, pressure, and chemical attack resistance (gas and liquids)
·Extreme hardness
·Excellent electrical insulation
·Relatively lightweight
Application:
Because zirconia has good properties of elasticity module and high hardness, as well as the above good properties, the parts made from zirconia are often used as mechanical or pump seal plate or disc.
About Us
Suzhou Jingci Super Hard Materials Co., Ltd has specialized in precision ceramics for more than twenty years and has rich experiences in designing and developing technical ceramic solutions for a wide variety of applications. Jingci has the capability to provide customers with expertise to make sure the best design and materials are made for their specific application and needs