Main component:96% Aluminium
Young’s Modulus (dynamic)/Elasticity Modules:360 Gpa
Vickers Hardness:1600-2200 HV0.5
Main component:zirconia
Gross density:6g/cm^3
Coefficient of Linear Expansion (20–400°C):10 10^–6/℃
Material:Zirconium
Density:6g/cm^3
Compressive Strength:3900Mpa (Psix103)
Main component:99% Al2O3
Gross density:3.8-3.9g/g/cm^3
Flexural Strength:430 Mpa (Psi*103)
Main component:zirconia
Gross density:6g/cm^3
Flexural Strength:1000 Mpa (Psi*103)
Gross density:3.8-3.9g/g/cm^3
Material:99% Al2O3
Flexural Strength:430 Mpa (Psi*103)
Thermal Shock Resistance:270℃ Tc
Thermal Expanding Coefficient:10 (1x10^-6/℃)
Thermal Conductivity:4 W/mK
Fundamental properties:High hardness, good wear resistance
Main component:zirconia
Flexural Strength:1000 Mpa (Psi*103)
Material grade (%Al2O3 content):96%
Porosity (apparent):0
Color:white
Main component:zirconium
Color:White
Thermal Conductivity:4 W/mK
Main ingredient:Yttria-stabilized zirconium
Gross density:6g/cm^3
Flexural Strength:1000 Mpa (Psi*103)
Material:99% aluminium
Material density:3.8-3.9g/g/cm^3
Vickers Hardness:1600-2200 HV0.5