Product Details:
|
| Name: | Ceramic Mechanical Seal | Usage: | Machinery |
|---|---|---|---|
| Color: | As Picture | Feature: | Low Friction |
| Vickers Hardness: | Alumina 1800-2000 HV; Zirconia ≈1300 HV; Silicon Carbon ≈2500HV | Fracture Toughness: | Alumina ≈5 (Mpa M1/2) ; Zirconia 7 (Mpa M1/2) |
| Compressive Strength: | Alumina ＞3200 (Mpa Psi*103); Zirconia ≈3900 (Mpa Psi*103)；Silicon Carbon 2200 (Mpa Psi*103) | Thermal Expending Coefficient: | Alumina 7.8-8.2 （1*10^-6/℃）；Silicon Carbon ≈4.5 （1*10^-6/℃） |
| High Light: | 2200HV Ceramic Pump Seal,Al2O3 Ceramic Pump Seal,Al2O3 ceramic mechanical seal |
||
Alumina Ceramic Seal Component for Machinery
Usage
1. Mechanical Seal
2. Heat Exchanger
3. Armour Plate
4. Ball Vlave Parts
5. Pump Components
6. Semiconductor
7. Metallurgical Engineering
8. Fixed and Moving Turbine Components
| Ceramic 95% | |
| Alumina | |
| Fundamental properties | High hardness, good wear resistance under abrasion,low electrical conductivity,good value for money |
| Main component | 95% Al2O3 |
| Gross density | 3.7g/cm^3 |
| Flexural Strength | 400 Mpa (Psi*103) |
| Compressive Strength | 3100Mpa (Psix103) |
| Fracture Toughness | 5 Mpa m1/2 |
| Young’s Modulus (dynamic)/Elasticity Modules | 300 Gpa |
| Vickers Hardness | 1500-2200 HV |
| Thermal Conductivity | 28 W/mK |
| Coefficient of Linear Expansion (20–400°C) |
7.5 10^–6 K–1 |
| Maximum Operating Temperature | 1400 ℃ |
| Thermal Expanding Coefficient | 7.5 (1x10^-6/℃) |
| Thermal Shock Resistance | 250℃ Tc |
| Disruptive Strength | KV/mm,DC ≥20 |
| Acid Resistance | mg/cm^2 ≤0.7 |
| Alkali Resistance | mg/cm^2 ≤0.2 |
| Wear Resistance | g/cm^2 ≤0.1 |
| Dielectric Strength | 9.0 εr(20℃ ,1MHz) |
| Dielectric Constant | 9.2 1MHz 25° |
| Tensile Strength | 51KN |
| Volume Resistivity | ＞10^15 100° |
| Water Absorption | 0 |
| Specific Heat Capacity | 0.78x10^3 J/(kg.K) |
Advantages of zirconia parts:
·High wear, heat, pressure, and chemical attack resistance (gas and liquids)
·Extreme hardness
·Excellent electrical insulation
·Relatively lightweight
Application:
Because zirconia has good properties of elasticity module and high hardness, as well as the above good properties, the parts made from zirconia are often used as mechanical or pump seal plate or disc.
About Us
Suzhou Jingci Super Hard Materials Co., Ltd has specialized in precision ceramics for more than twenty years and has rich experiences in designing and developing technical ceramic solutions for a wide variety of applications. Jingci has the capability to provide customers with expertise to make sure the best design and materials are made for their specific application and needs